SABIC® LLDPE 6218BE

线性低密度聚乙烯

Saudi Basic Industries Corporation (SABIC)

Technical Data

 

产品说明

SABIC® LLDPE 6218BE is a hexene linear low density polyethylene resin for cast film applications. The product has been specially formulated for optimum thermal stability at high temperatures used in cast film extrusion. Cast films produced from SABIC® LLDPE 6218BE exhibit excellent optical properties, improved toughness, puncture resistance and tear strength. The suffix E denotes European origin

 

SABIC® LLDPE 6218BE resin is recommended for pallet stretch wrap (pre-stretch), high performance draw down films and other mono layer and coextruded film applications where high strength is required. The grade is also suggested for blending with ethylene/butene copolymer LLDPE and LDPE for improving strength.

 

The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Processing - Cast Film (English)

•  Technical Datasheet (English)

搜索 UL 黄卡 •  Saudi Basic Industries Corporation (SABIC)

供货地区 • 欧洲

添加剂 • 抗氧化性

• 光学性能 • 抗氧化性 • 韧性良好

特性 • 己烯共聚单体 • 良好的撕裂强度

• 抗穿孔性 • 热稳定性，良好

用途 • 混合 • 拉伸缠绕 • 流延薄膜

形式 • 粒子

加工方法 • 流延薄膜

 

物理性能 额定值单位制 测试方法

密度 0.920g/cm³ ISO 1183/A

熔流率（熔体流动速率） (190°C/2.16 kg) 2.2g/10 min ISO 1133

薄膜 额定值单位制 测试方法

薄膜厚度 - 经测试 20µm

Elastic Recovery 3 (20.0 µm) 56% ASTM D5459

Protrusion Puncture Resistance 3 (20.0 µm) 1.90J ASTM D5748

Retention Force - 60 sec 3 (20.0 µm) 990g

Stress Retention 3 (20.0 µm) 77% ASTM D5459

Ultimate Pre-stretch Level 3 (20.0 µm) 260%

热性能 额定值单位制 测试方法

维卡软化温度 103°C ISO 306/A

溶融温度（DSC） 125°C 内部方法

光学性能 额定值单位制 测试方法

光泽度 (45°, 20.0 µm, 铸造薄膜) 90 ASTM D2457

雾度 (20.0 µm, 铸造薄膜) 2.2% ASTM D1003A

补充信息 额定值单位制 测试方法

Dart Impact 3 (20.0 µm) 27.0J/cm ISO 7765-2

Peel Cling 3 ASTM D5458

0% pre-stretch : 20.0 µm 229.4g/2.5 cm

200% pre-stretch : 20.0 µm 76.5g/2.5 cm

Tear Strength - TD 3 (20.0 µm) 272.0kN/m ISO 6383-2

 

SABIC® LLDPE 6218BE

线性低密度聚乙烯

Saudi Basic Industries Corporation (SABIC)

 

Film properties

Properties are determined on 20 µm cast stretch film produced on a 2 m commercial cast stretch film line: melt temperature 270 °C, chill roll temperature 20 °C and a line speed of 450 m/min.

 

Processing conditions

SABIC® LLDPE 6218BE is extrudable with conventional cast film extrusion equipment. Temperatures 250-300 °C.

 

挤出 额定值单位制

熔体温度 250 到 300°C

 

 

 

 

 

 

 

 

东莞市双帮塑胶原料有限公司大量销售塑料线性低密度聚乙烯  SABIC 基础创新塑料(美国) SABIC® LLDPE 6218BE因为塑料价格行情每天都有新的变化前天的报价不等于今天的报价。如果需要新的价格请电：13549213581，肖生。