抗氧化性, 低速凝固晶点, 食品接触的合规性, 耐油脂性能, 吸水低或不吸水, 薄膜, 母料, 食品包装, 涂层应用, 复合, 挤出涂层, 流延薄膜

SABIC® HDPE 0863F

高密度聚乙烯

Saudi Basic Industries Corporation (SABIC)

Technical Data

 

产品说明

High density polyethylene for Extrusion coating:

• SABIC® HDPE 0863F resin is a homopolymer with an exceptional high density manufactured by gas phase technology. The grade offers high stiffness, high temperature resistance, low water vapour transmission and relatively high grease resistance. The resin has an extreme low gel level. Because of the linear character it is advisable to use the material in combination with extrusion coating LDPE grades like SABIC® LDPE nExCoat5 in order to improve extrusion coating processability and maintain web stability. 

• Application: SABIC® HDPE 0863F is typically used for food packaging, release paper and photographic paper. 

 

High density polyethylene for masterbatch compounding:

• SABIC® HDPE 0863F is a special homopolymer HDPE grade with a very low gel level and good intrinsic stability. 

• Application: SABIC® HDPE 0863F is specially suited for masterbatches in extrusion coating, in HDPE layers. Further as masterbatch in general or specific HDPE applications, when stiffness, combined with good flow properties are required, such as injection moulding and film extrusion. 

 

The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.

 

总体

 

材料状态 • 已商用：当前有效

• Processing - BOPP Film (English) 

• Processing - Cast Film (English) 

资料 1 •  Processing - Tape (English)

•  Technical Datasheet (English)

•  Technical Datasheet (English)

搜索 UL 黄卡 •  Saudi Basic Industries Corporation (SABIC)

供货地区 • 欧洲

添加剂 • 抗氧化性

特性 • 低速凝固晶点 • 耐热性，高 • 食品接触的合规性

• 刚性，高 • 耐油脂性能 • 吸水低或不吸水

用途 • 薄膜 • 母料 • 涂层应用

• 离型纸 • 食品包装

机构评级 • EC 2023/2006 • FDA 21 CFR 177.1520

加工方法 • 复合 • 挤出涂层 • 流延薄膜

物理性能 额定值(英制) 额定值(公制) 测试方法

密度 0.964g/cm³ 0.964g/cm³ ISO 1183

熔流率（熔体流动速率） (190°C/2.16 kg) 8.0g/10 min 8.0g/10 min ISO 1133

薄膜 额定值(英制) 额定值(公制) 测试方法

薄膜厚度 - 经测试 0.98mil 25µm

拉伸模量 ISO 527-3

MD : 0.98 mil (25 µm), 铸造薄膜 84100psi 580MPa

TD : 0.98 mil (25 µm), 铸造薄膜 84100psi 580MPa

拉伸应力 ISO 527-3

MD : 屈服, 0.98 mil (25 µm), 铸造薄膜 3770psi 26.0MPa

TD : 屈服, 0.98 mil (25 µm), 铸造薄膜 3480psi 24.0MPa

MD : 断裂, 0.98 mil (25 µm), 铸造薄膜 3190psi 22.0MPa

TD : 断裂, 0.98 mil (25 µm), 铸造薄膜 2610psi 18.0MPa

伸长率 ISO 527-3

MD : 断裂, 0.98 mil (25 µm), 铸造薄膜 700% 700%

TD : 断裂, 0.98 mil (25 µm), 铸造薄膜 800% 800%

水气透过率 内部方法

100°F (38°C), 100% RH, 0.98 mil (25 µm), 0.26g/100 in²/24 hr 4.0g/m²/24 hr

铸造薄膜

 

SABIC® HDPE 0863F

高密度聚乙烯

Saudi Basic Industries Corporation (SABIC)

薄膜 额定值(英制) 额定值(公制) 测试方法

Oxygen Permeability 3 内部方法

73°F (23°C), 1.0 mil (25.0 µm) 0.10cm³/cm²/bar 0.10cm³/cm²/bar

热性能 额定值(英制) 额定值(公制) 测试方法

维卡软化温度 266°F 130°C ISO 306/A

溶融温度（DSC） 273°F 134°C DIN 53765

Enthalpy Change 224J/g 224J/g DIN 53765

 

 

 

 

 

 

东莞市双帮塑胶原料有限公司大量销售塑料高密度聚乙烯  SABIC HDPE 基础创新塑料(美国) SABIC® HDPE 0863F因为塑料价格行情每天都有新的变化前天的报价不等于今天的报价。如果需要新的价格请电：13549213581，肖生。