ASTALON™ H3000R
聚碳酸酯
Marplex Australia Pty. Ltd.
Technical Data
产品说明
ASTALON™ H3000R / H3001R / H3003R are the low viscosity (ultra high melt flow) grades in the ASTALON™ range and are well suited to intricate or "difficult to fill" injection moulding applications which require a mould release agent (R). Offering an excellent balance of transparency, toughness, heat resistance, flame retardancy and processability, typical applications include drinking tumblers, food processors and other kitchen appliances and domestic serving trays.
Note: [ Standard grade = H3000R ] / [ FDA approved = H3001R ] / [ Steam resistant = H3003R ].
总体
材料状态 • 已商用：当前有效
资料 1 • Technical Datasheet (English)
Search for UL Yellow Card • Marplex Australia Pty. Ltd.
供货地区 • 北美洲 • 南美洲 • 亚太地区
添加剂 • 脱模
• 低粘度 • 耐热性，中等 • 阻燃性能
性能特点 • 可加工性，良好 • 韧性良好
• 流动性高 • 中等透明度
用途 • 电器用具 • 非特定食品应用
加工方法 • 注射成型
物理性能 额定值单位制 测试方法
比重 1.20g/cm³ ASTM D792
熔流率 (300°C/1.2 kg) 28g/10 min ASTM D1238
收缩率 - 流动 (3.00 mm) 0.40 到 0.80% ASTM D955
吸水率 (24 hr) 0.24% ASTM D570
机械性能 额定值单位制 测试方法
抗张强度 3 (3.20 mm) 62.0MPa ASTM D638
伸长率 3 (断裂, 3.20 mm) 100% ASTM D638
弯曲模量 4 (6.40 mm) 2300MPa ASTM D790
弯曲强度 4 (6.40 mm) 87.0MPa ASTM D790
冲击性能 额定值单位制 测试方法
悬壁梁缺口冲击强度 (3.20 mm) 250J/m ASTM D256
落锤冲击 (3.20 mm) 65.0J ASTM D3029
硬度 额定值单位制 测试方法
洛氏硬度 (R 计秤) 123 ASTM D785
热性能 额定值单位制 测试方法
热变形温度 ASTM D648
0.45 MPa, 未退火, 6.40 mm 132°C
1.8 MPa, 未退火, 6.40 mm 128°C
线形膨胀系数 - 流动 0.000060 到 0.000070cm/cm/°C ASTM D696
电气性能 额定值单位制 测试方法
体积电阻率 2.1E+16ohm•cm ASTM D257
介电常数 2.85 ASTM D150
可燃性 额定值单位制 测试方法
UL 阻燃等级 (1.60 mm) V-2 UL 94
光学性能 额定值单位制 测试方法
透射率 (总计, 3000 µm) 85.0% ASTM D1003
注射 额定值单位制
干燥温度 120 到 125°C
干燥时间 4.0 到 6.0hr
螺筒后部温度 230 到 245°C
1 / 3
ASTALON™ H3000R
聚碳酸酯
Marplex Australia Pty. Ltd.
注射 额定值单位制
螺筒中部温度 240 到 255°C
螺筒前部温度 250 到 265°C
加工（熔体）温度 240 到 270°C
模具温度 60.0 到 110°C
注塑温度 60.0 到 140MPa
注射速度 中等
背压 0.100 到 0.500MPa
螺杆转速 40 到 60rpm
合模力 4.0 到 8.0kN/cm²
备注